Anti Corrosion Water Based Epoxy Resin For Two Components Metal

WL-213 Waterborne Epoxy Resin

Physical Property:

Item	Value	Testing Method
Appearance	Milky white emulsion	Visual
Solid content	50±2%	30min@120℃
Viscosity(mPa.s)	≤2000	NDJ-79 Rotational viscometer
PH	7-8	PH Meter
TG/℃	0.18-0.22	Aceton* hydrochloride method

Performance:

• Non-ionic self-emulsifying type
• Small emulsion particle size
• Good film forming performance
• Low VOC content

• Epoxy gray paint performance

Gray paint	Surface Drying	Real Drying	Hardness	Flexibility	Adhesion	Construction Time Limit	Impact Resistance
WL-213+WL-140	35mins	5h	≥H	1grade	0grade	≥4h	50cm

• Carbon steel plate (sand paper polishing)

◆ 80℃ X 120 minutes flash dry

◆ 14 days natural dry curing period

◆ Film thickness 50~60μm

◆ Salt spray resistance>800hrs

• Epoxy varnish performance comparison

• Alkali resistance performance:

23-29um, baking at 80℃ for 30 minutes,

0.1mol/L NaOH aqueous solution

After 64h of alkali resistance testing :

Has spots Almost no spots

(AP resin) (WL-213/WL-140)

• Acid resistance:

Thickness of film is 23-29um, back at 80℃ for 30 minutes,

0.1mol/L H2SO4 aqueous solution

Large bubbles on the board Small bubbles or no bubbles

( AP resin) (WL-213/WL-140)

3.Epoxy white paint performance comparison

Gray paint	Surface Drying	Real Drying	Hardness	Flexibility	Adhesion	Construction Time Limit	Impact Resistance
Comparative resin	37mins	5.4h	H	1 grade	0 grade		50cm
WL-213+WL-140	35mins	5h	H	1 grade	0 grade	≥4h	50cm

• Ethanol wiping Resistance performance:

Thickness of film is 23-26um, back at 80℃ for 30 minutes

Failed after 30 wipes Pass after 50 wipes

(Contrast resin) (WL-213/WL-140)

• Alkali resistance performance:

The film thickness all is 23-29um, after 80℃X30 minutes

Put it into 0.1mol/L NaOH aqueous solution and soak for 64 hours

The paint surface of WL-213/WL-140 is slightly dull

The paint surface of the contrast resin has more large bubbles

After 64h of alkali resistance testing :

( AP resin) (WL-213/WL-140)

• Acid resistance performance:

-The thickness of the film is 23-29um, after drying at 80℃ for 30 minutes

-Put into 0.1mol/L sulfuric acid aqueous solution

-After 64 hours of soaking

-The paint surface of WL-213/WL-140 is slightly dull

-The paint surface of the contrast resin has large bubbles and cracks

( contrast resin) (WL-213/WL-140)

• Salt spray resistance performance:

-The film thickness is 50-60um

-Test after 7 days in a constant temperature and humidity environment

-After 64 hours of salt spray resistance test, the white paint board of the contrast resin is corroded more

( contrast resin) (WL-213/WL-140)

Special Tips

This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.